AISI 8650 |
 |
|
| Conditions | Tensile Properties |
| T (°C) | Treatment |
| 25 |
annealed at 795°C |
Tensile Strength (MPa) |
715.7 |
| Yield Strength (MPa) |
386.1 |
| Elongation (%) |
22.5 |
| Reduction in Area (%) |
46.4 |
| 25 |
normalized at 870°C |
Tensile Strength (MPa) |
1023.9 |
| Yield Strength (MPa) |
688.1 |
| Elongation (%) |
14.0 |
| Reduction in Area (%) |
40.4 |
| 25 |
oil quenched, fine grained, tempered at 205°C |
Tensile Strength (MPa) |
1937 |
| Yield Strength (MPa) |
1675 |
| Elongation (%) |
10 |
| Reduction in Area (%) |
38 |
| 25 |
oil quenched, fine grained, tempered at 315°C |
Tensile Strength (MPa) |
1724 |
| Yield Strength (MPa) |
1551 |
| Elongation (%) |
10 |
| Reduction in Area (%) |
40 |
| 25 |
oil quenched, fine grained, tempered at 425°C |
Tensile Strength (MPa) |
1448 |
| Yield Strength (MPa) |
1324 |
| Elongation (%) |
12 |
| Reduction in Area (%) |
45 |
| 25 |
oil quenched, fine grained, tempered at 540°C |
Tensile Strength (MPa) |
1172 |
| Yield Strength (MPa) |
1055 |
| Elongation (%) |
15 |
| Reduction in Area (%) |
51 |
| 25 |
oil quenched, fine grained, tempered at 650°C |
Tensile Strength (MPa) |
965 |
| Yield Strength (MPa) |
827 |
| Elongation (%) |
20 |
| Reduction in Area (%) |
58 |
|