AA 6061 |
 |
|
| Conditions | Tensile Properties |
| T (°C) | Treatment |
| 25 |
O (Alclad) |
Tensile Strength (MPa) |
115 |
| Yield Strength (MPa) |
48 |
| Elongation (%) |
25 |
| Reduction in Area (%) |
|
| 25 |
O |
Tensile Strength (MPa) |
125 |
| Yield Strength (MPa) |
55 |
| Elongation (%) |
25 |
| Reduction in Area (%) |
|
| 25 |
T4 (Alclad) |
Tensile Strength (MPa) |
230 |
| Yield Strength (MPa) |
130 |
| Elongation (%) |
22 |
| Reduction in Area (%) |
|
| 25 |
T4 |
Tensile Strength (MPa) |
240 |
| Yield Strength (MPa) |
145 |
| Elongation (%) |
22 |
| Reduction in Area (%) |
|
| 25 |
T451 (Alclad) |
Tensile Strength (MPa) |
230 |
| Yield Strength (MPa) |
130 |
| Elongation (%) |
22 |
| Reduction in Area (%) |
|
| 25 |
T451 |
Tensile Strength (MPa) |
240 |
| Yield Strength (MPa) |
145 |
| Elongation (%) |
22 |
| Reduction in Area (%) |
|
| 25 |
T6 (Alclad) |
Tensile Strength (MPa) |
290 |
| Yield Strength (MPa) |
255 |
| Elongation (%) |
12 |
| Reduction in Area (%) |
|
| 25 |
T6 |
Tensile Strength (MPa) |
310 |
| Yield Strength (MPa) |
275 |
| Elongation (%) |
12 |
| Reduction in Area (%) |
|
| 25 |
T651 (Alclad) |
Tensile Strength (MPa) |
290 |
| Yield Strength (MPa) |
255 |
| Elongation (%) |
12 |
| Reduction in Area (%) |
|
| 25 |
T651 |
Tensile Strength (MPa) |
310 |
| Yield Strength (MPa) |
275 |
| Elongation (%) |
12 |
| Reduction in Area (%) |
|
|