AISI 6150 |
 |
|
| Conditions | Tensile Properties |
| T (°C) | Treatment |
| 25 |
annealed at 815°C |
Tensile Strength (MPa) |
667.4 |
| Yield Strength (MPa) |
412.3 |
| Elongation (%) |
23.0 |
| Reduction in Area (%) |
48.4 |
| 25 |
normalized at 870°C |
Tensile Strength (MPa) |
939.8 |
| Yield Strength (MPa) |
615.7 |
| Elongation (%) |
21.8 |
| Reduction in Area (%) |
61.0 |
| 25 |
oil quenched, fine grained, tempered at 205°C |
Tensile Strength (MPa) |
1931 |
| Yield Strength (MPa) |
1689 |
| Elongation (%) |
8 |
| Reduction in Area (%) |
38 |
| 25 |
oil quenched, fine grained, tempered at 315°C |
Tensile Strength (MPa) |
1724 |
| Yield Strength (MPa) |
1572 |
| Elongation (%) |
8 |
| Reduction in Area (%) |
39 |
| 25 |
oil quenched, fine grained, tempered at 425°C |
Tensile Strength (MPa) |
1434 |
| Yield Strength (MPa) |
1331 |
| Elongation (%) |
10 |
| Reduction in Area (%) |
43 |
| 25 |
oil quenched, fine grained, tempered at 540°C |
Tensile Strength (MPa) |
1158 |
| Yield Strength (MPa) |
1069 |
| Elongation (%) |
13 |
| Reduction in Area (%) |
50 |
| 25 |
oil quenched, fine grained, tempered at 650°C |
Tensile Strength (MPa) |
945 |
| Yield Strength (MPa) |
841 |
| Elongation (%) |
17 |
| Reduction in Area (%) |
58 |
|