AA 2024 |
 |
|
| Conditions | Tensile Properties |
| T (°C) | Treatment |
| 25 |
O |
Tensile Strength (MPa) |
185 |
| Yield Strength (MPa) |
76 |
| Elongation (%) |
20 |
| Reduction in Area (%) |
|
| 25 |
O (Alclad) |
Tensile Strength (MPa) |
180 |
| Yield Strength (MPa) |
76 |
| Elongation (%) |
20 |
| Reduction in Area (%) |
|
| 25 |
T (Alclad) |
Tensile Strength (MPa) |
450 |
| Yield Strength (MPa) |
310 |
| Elongation (%) |
18 |
| Reduction in Area (%) |
|
| 25 |
T3 |
Tensile Strength (MPa) |
485 |
| Yield Strength (MPa) |
345 |
| Elongation (%) |
18 |
| Reduction in Area (%) |
|
| 25 |
T351 (Alclad) |
Tensile Strength (MPa) |
440 |
| Yield Strength (MPa) |
290 |
| Elongation (%) |
19 |
| Reduction in Area (%) |
|
| 25 |
T351 |
Tensile Strength (MPa) |
470 |
| Yield Strength (MPa) |
325 |
| Elongation (%) |
20 |
| Reduction in Area (%) |
|
| 25 |
T361 (Alclad) |
Tensile Strength (MPa) |
460 |
| Yield Strength (MPa) |
365 |
| Elongation (%) |
11 |
| Reduction in Area (%) |
|
| 25 |
T361 |
Tensile Strength (MPa) |
495 |
| Yield Strength (MPa) |
395 |
| Elongation (%) |
13 |
| Reduction in Area (%) |
|
| 25 |
T4 (Alclad) |
Tensile Strength (MPa) |
440 |
| Yield Strength (MPa) |
290 |
| Elongation (%) |
19 |
| Reduction in Area (%) |
|
| 25 |
T4 |
Tensile Strength (MPa) |
470 |
| Yield Strength (MPa) |
325 |
| Elongation (%) |
20 |
| Reduction in Area (%) |
|
| 25 |
T81 (Alclad) |
Tensile Strength (MPa) |
450 |
| Yield Strength (MPa) |
415 |
| Elongation (%) |
6 |
| Reduction in Area (%) |
|
| 25 |
T851 (Alclad) |
Tensile Strength (MPa) |
450 |
| Yield Strength (MPa) |
415 |
| Elongation (%) |
6 |
| Reduction in Area (%) |
|
| 25 |
T861 (Alclad) |
Tensile Strength (MPa) |
485 |
| Yield Strength (MPa) |
455 |
| Elongation (%) |
6 |
| Reduction in Area (%) |
|
|