AISI 1095 |
 |
|
| Conditions | Tensile Properties |
| T (°C) | Treatment |
| 25 |
annealed at 790°C |
Tensile Strength (MPa) |
656.7 |
| Yield Strength (MPa) |
379.2 |
| Elongation (%) |
13.0 |
| Reduction in Area (%) |
20.6 |
| 25 |
normalized at 900°C |
Tensile Strength (MPa) |
1013.5 |
| Yield Strength (MPa) |
499.9 |
| Elongation (%) |
9.5 |
| Reduction in Area (%) |
13.5 |
| 25 |
oil quenched, fine grained, tempered at 205°C |
Tensile Strength (MPa) |
1489 |
| Yield Strength (MPa) |
1048 |
| Elongation (%) |
10 |
| Reduction in Area (%) |
31 |
| 25 |
oil quenched, fine grained, tempered at 205°C |
Tensile Strength (MPa) |
1289 |
| Yield Strength (MPa) |
827 |
| Elongation (%) |
10 |
| Reduction in Area (%) |
30 |
| 25 |
oil quenched, fine grained, tempered at 315°C |
Tensile Strength (MPa) |
1462 |
| Yield Strength (MPa) |
1034 |
| Elongation (%) |
11 |
| Reduction in Area (%) |
33 |
| 25 |
oil quenched, fine grained, tempered at 315°C |
Tensile Strength (MPa) |
1262 |
| Yield Strength (MPa) |
813 |
| Elongation (%) |
10 |
| Reduction in Area (%) |
30 |
| 25 |
oil quenched, fine grained, tempered at 425°C |
Tensile Strength (MPa) |
1372 |
| Yield Strength (MPa) |
958 |
| Elongation (%) |
13 |
| Reduction in Area (%) |
35 |
| 25 |
oil quenched, fine grained, tempered at 425°C |
Tensile Strength (MPa) |
1213 |
| Yield Strength (MPa) |
772 |
| Elongation (%) |
12 |
| Reduction in Area (%) |
32 |
| 25 |
oil quenched, fine grained, tempered at 540°C |
Tensile Strength (MPa) |
1089 |
| Yield Strength (MPa) |
676 |
| Elongation (%) |
15 |
| Reduction in Area (%) |
37 |
| 25 |
oil quenched, fine grained, tempered at 540°C |
Tensile Strength (MPa) |
1138 |
| Yield Strength (MPa) |
758 |
| Elongation (%) |
15 |
| Reduction in Area (%) |
40 |
| 25 |
oil quenched, fine grained, tempered at 650°C |
Tensile Strength (MPa) |
896 |
| Yield Strength (MPa) |
552 |
| Elongation (%) |
21 |
| Reduction in Area (%) |
47 |
| 25 |
oil quenched, fine grained, tempered at 650°C |
Tensile Strength (MPa) |
841 |
| Yield Strength (MPa) |
586 |
| Elongation (%) |
20 |
| Reduction in Area (%) |
47 |
| 25 |
rolled |
Tensile Strength (MPa) |
965.3 |
| Yield Strength (MPa) |
572.3 |
| Elongation (%) |
9.0 |
| Reduction in Area (%) |
18.0 |
|