| Conditions | Tensile Properties |
| T (°C) | Treatment |
| 25 |
annealed at 825°C |
Tensile Strength (MPa) |
675.7 |
| Yield Strength (MPa) |
357.1 |
| Elongation (%) |
22.0 |
| Reduction in Area (%) |
43.7 |
| 25 |
normalized at 870°C |
Tensile Strength (MPa) |
870.8 |
| Yield Strength (MPa) |
529.5 |
| Elongation (%) |
20.7 |
| Reduction in Area (%) |
58.7 |
| 25 |
oil quenched, fine grained, tempered at 205°C |
Tensile Strength (MPa) |
1944 |
| Yield Strength (MPa) |
1731 |
| Elongation (%) |
5 |
| Reduction in Area (%) |
37 |
| 25 |
oil quenched, fine grained, tempered at 315°C |
Tensile Strength (MPa) |
1737 |
| Yield Strength (MPa) |
1586 |
| Elongation (%) |
6 |
| Reduction in Area (%) |
40 |
| 25 |
oil quenched, fine grained, tempered at 425°C |
Tensile Strength (MPa) |
1448 |
| Yield Strength (MPa) |
1310 |
| Elongation (%) |
9 |
| Reduction in Area (%) |
47 |
| 25 |
oil quenched, fine grained, tempered at 540°C |
Tensile Strength (MPa) |
1124 |
| Yield Strength (MPa) |
1034 |
| Elongation (%) |
15 |
| Reduction in Area (%) |
54 |
| 25 |
oil quenched, fine grained, tempered at 650°C |
Tensile Strength (MPa) |
807 |
| Yield Strength (MPa) |
814 |
| Elongation (%) |
20 |
| Reduction in Area (%) |
60 |