| Conditions | Tensile Properties |
| T (°C) | Treatment |
| 25 |
annealed at 845°C |
Tensile Strength (MPa) |
774.3 |
| Yield Strength (MPa) |
486.1 |
| Elongation (%) |
21.7 |
| Reduction in Area (%) |
41.1 |
| 25 |
normalized at 900°C |
Tensile Strength (MPa) |
932.9 |
| Yield Strength (MPa) |
579.2 |
| Elongation (%) |
19.7 |
| Reduction in Area (%) |
43.4 |
| 25 |
oil quenched, fine grained, tempered at 205°C |
Tensile Strength (MPa) |
2103 |
| Yield Strength (MPa) |
2048 |
| Elongation (%) |
1 |
| Reduction in Area (%) |
3 |
| 25 |
oil quenched, fine grained, tempered at 315°C |
Tensile Strength (MPa) |
1937 |
| Yield Strength (MPa) |
1793 |
| Elongation (%) |
4 |
| Reduction in Area (%) |
10 |
| 25 |
oil quenched, fine grained, tempered at 425°C |
Tensile Strength (MPa) |
1606 |
| Yield Strength (MPa) |
1489 |
| Elongation (%) |
8 |
| Reduction in Area (%) |
22 |
| 25 |
oil quenched, fine grained, tempered at 540°C |
Tensile Strength (MPa) |
1255 |
| Yield Strength (MPa) |
1103 |
| Elongation (%) |
15 |
| Reduction in Area (%) |
32 |
| 25 |
oil quenched, fine grained, tempered at 650°C |
Tensile Strength (MPa) |
993 |
| Yield Strength (MPa) |
814 |
| Elongation (%) |
20 |
| Reduction in Area (%) |
42 |