| AISI S1 | |
 | |
| Conditions | Tensile Properties | ||
| T (°C) | Treatment | ||
| 25 | annealed | Tensile Strength (MPa) | 690 |
| Yield Strength (MPa) | 415 | ||
| Elongation (%) | 24 | ||
| Reduction in Area (%) | 52 | ||
| 25 | oil quenched from 930°C, single tempered at 205°C | Tensile Strength (MPa) | 2070 |
| Yield Strength (MPa) | 1895 | ||
| Elongation (%) | |||
| Reduction in Area (%) | |||
| 25 | oil quenched from 930°C, single tempered at 315°C | Tensile Strength (MPa) | 2030 |
| Yield Strength (MPa) | 1860 | ||
| Elongation (%) | 4 | ||
| Reduction in Area (%) | 12 | ||
| 25 | oil quenched from 930°C, single tempered at 425°C | Tensile Strength (MPa) | 1790 |
| Yield Strength (MPa) | 1690 | ||
| Elongation (%) | 5 | ||
| Reduction in Area (%) | 17 | ||
| 25 | oil quenched from 930°C, single tempered at 540°C | Tensile Strength (MPa) | 1680 |
| Yield Strength (MPa) | 1525 | ||
| Elongation (%) | 9 | ||
| Reduction in Area (%) | 23 | ||
| 25 | oil quenched from 930°C, single tempered at 650°C | Tensile Strength (MPa) | 1345 |
| Yield Strength (MPa) | 1240 | ||
| Elongation (%) | 12 | ||
| Reduction in Area (%) | 37 | ||