Materials Design Center Processes Unit Conversion Formulas Mathematics
 Calculators Discussion Forum Trade Publications Directory Service
World Pumps

Major news, innovation and real-life applications for pumps and ancillary equipment.

Offshore

International news and technology for marine/offshore operations around the world.

Power Transmission

Gear drives, bearings, motors, clutches, couplings, machine controls, sensors and components.

Essentials of Manufacturing

Information, coverage of important developments and expert commentary in manufacturing.

more free magazines
Glossary » Materials » Alloys » Steel » Alloy Steel » AISI 4028H
AISI 4028H is an H-Steel grade Alloy Steel. It is commonly called AISI 4028H Molybdenum steel. It is composed of (in weight percentage) 0.24-0.30% Carbon (C), 0.60-1.00% Manganese (Mn), 0.20-0.30% Molybdenum (Mo), 0.035% Phosphorus (P), 0.040% Sulfur (S), 0.15-0.30% Silicon (Si), and the base metal Iron (Fe). Other designations of AISI 4028H alloy steel include UNS H40280 and AISI 4028H.
Steel is the common name for a large family of iron alloys. Steels can either be cast directly to shape, or into ingots which are reheated and hot worked into a wrought shape by forging, extrusion, rolling, or other processes. Wrought steels are the most common engineering material used, and come in a variety of forms with different finishes and properties. Alloy steels are steels that exceed the element limits for Carbon steels. However, steels containing more than 3.99% chromium are classified differently as stainless and tool steels. Alloy steels also includes steels that contain elements not found in carbon steels such as nickel, chromium (up to 3.99%), cobalt, etc.

The typical elastic modulus of alloy steels at room temperature (25°C) ranges from 190 to 210 GPa. The typical density of alloy steels is about 7.85 g/cm3. The typical tensile strength varies between 758 and 1882 MPa. The wide range of ultimate tensile strength is largely due to different heat treatment conditions.