Glossary » Materials » Alloys » Steel » Carbon Steel » AISI 1522H
AISI 1522H is an H-Steel grade Carbon Steel. It is composed of (in weight percentage) 0.17-0.25% Carbon (C), 1.00-1.50% Manganese (Mn), 0.04%(max) Phosphorus (P), 0.05%(max) Sulfur (S), 0.15-0.30% Silicon (Si), and the base metal Iron (Fe). Other designations of AISI 1522H carbon steel include UNS H15220 and AISI 1522H.
Steel is the common name for a large family of iron alloys. Steels can either be cast directly to shape, or into ingots which are reheated and hot worked into a wrought shape by forging, extrusion, rolling, or other processes. Wrought steels are the most common engineering material used, and come in a variety of forms with different finishes and properties. Carbon steels alloying elements do not exceed these limits: 1% carbon, 0.6% copper, 1.65% manganese, 0.4% phosphorus, 0.6% silicon, and 0.05% sulfur.

The typical elastic modulus of carbon steels at room temperature (25°C) ranges from 190 to 210 GPa. The typical density of carbon steels is about 7.85 g/cm3. The typical tensile strength varies between 276 and 1882 MPa. The wide range of ultimate tensile strength is largely due to different heat treatment conditions.

Related Pages
Injection Molding Design Guide

Guide for high quality and cost-effective plastic injection molding.

Metal 3D Printing Design Guide

Direct Metal Laser Sintering (DMLS) 3D printing for parts with reduced cost and little waste.

CNC Machining Design Guide