| Conditions | Tensile Properties |
| T (°C) | Treatment |
| 25 |
annealed at 865°C |
Tensile Strength (MPa) |
560.5 |
| Yield Strength (MPa) |
360.6 |
| Elongation (%) |
28.2 |
| Reduction in Area (%) |
55.6 |
| 25 |
normalized at 870°C |
Tensile Strength (MPa) |
668.8 |
| Yield Strength (MPa) |
436.4 |
| Elongation (%) |
25.5 |
| Reduction in Area (%) |
59.5 |
| 25 |
water quenched, fine grained, tempered at 205°C |
Tensile Strength (MPa) |
1627 |
| Yield Strength (MPa) |
1462 |
| Elongation (%) |
10 |
| Reduction in Area (%) |
41 |
| 25 |
water quenched, fine grained, tempered at 315°C |
Tensile Strength (MPa) |
1496 |
| Yield Strength (MPa) |
1379 |
| Elongation (%) |
11 |
| Reduction in Area (%) |
43 |
| 25 |
water quenched, fine grained, tempered at 425°C |
Tensile Strength (MPa) |
1282 |
| Yield Strength (MPa) |
1193 |
| Elongation (%) |
13 |
| Reduction in Area (%) |
49 |
| 25 |
water quenched, fine grained, tempered at 540°C |
Tensile Strength (MPa) |
1034 |
| Yield Strength (MPa) |
910 |
| Elongation (%) |
17 |
| Reduction in Area (%) |
57 |
| 25 |
water quenched, fine grained, tempered at 650°C |
Tensile Strength (MPa) |
814 |
| Yield Strength (MPa) |
703 |
| Elongation (%) |
22 |
| Reduction in Area (%) |
64 |