| Conditions | Tensile Properties |
| T (°C) | Treatment |
| 25 |
annealed at 815°C |
Tensile Strength (MPa) |
655.0 |
| Yield Strength (MPa) |
417.1 |
| Elongation (%) |
25.7 |
| Reduction in Area (%) |
56.9 |
| 25 |
normalized at 870°C |
Tensile Strength (MPa) |
1020.4 |
| Yield Strength (MPa) |
655.0 |
| Elongation (%) |
17.7 |
| Reduction in Area (%) |
46.8 |
| 25 |
oil quenched, fine grained, tempered at 205°C |
Tensile Strength (MPa) |
1772 |
| Yield Strength (MPa) |
1641 |
| Elongation (%) |
8 |
| Reduction in Area (%) |
38 |
| 25 |
oil quenched, fine grained, tempered at 315°C |
Tensile Strength (MPa) |
1551 |
| Yield Strength (MPa) |
1434 |
| Elongation (%) |
9 |
| Reduction in Area (%) |
43 |
| 25 |
oil quenched, fine grained, tempered at 425°C |
Tensile Strength (MPa) |
1248 |
| Yield Strength (MPa) |
1138 |
| Elongation (%) |
13 |
| Reduction in Area (%) |
49 |
| 25 |
oil quenched, fine grained, tempered at 540°C |
Tensile Strength (MPa) |
951 |
| Yield Strength (MPa) |
834 |
| Elongation (%) |
18 |
| Reduction in Area (%) |
58 |
| 25 |
oil quenched, fine grained, tempered at 650°C |
Tensile Strength (MPa) |
758 |
| Yield Strength (MPa) |
655 |
| Elongation (%) |
22 |
| Reduction in Area (%) |
63 |