| Conditions | Tensile Properties |
| T (°C) | Treatment |
| 25 |
annealed at 810°C |
Tensile Strength (MPa) |
744.6 |
| Yield Strength (MPa) |
472.3 |
| Elongation (%) |
22.0 |
| Reduction in Area (%) |
49.9 |
| 25 |
normalized at 870°C |
Tensile Strength (MPa) |
1279.0 |
| Yield Strength (MPa) |
861.8 |
| Elongation (%) |
12.2 |
| Reduction in Area (%) |
36.3 |
| 25 |
oil quenched, fine grained, tempered at 205°C |
Tensile Strength (MPa) |
1875 |
| Yield Strength (MPa) |
1675 |
| Elongation (%) |
10 |
| Reduction in Area (%) |
38 |
| 25 |
oil quenched, fine grained, tempered at 315°C |
Tensile Strength (MPa) |
1724 |
| Yield Strength (MPa) |
1586 |
| Elongation (%) |
10 |
| Reduction in Area (%) |
40 |
| 25 |
oil quenched, fine grained, tempered at 425°C |
Tensile Strength (MPa) |
1469 |
| Yield Strength (MPa) |
1365 |
| Elongation (%) |
10 |
| Reduction in Area (%) |
44 |
| 25 |
oil quenched, fine grained, tempered at 540°C |
Tensile Strength (MPa) |
1172 |
| Yield Strength (MPa) |
1076 |
| Elongation (%) |
13 |
| Reduction in Area (%) |
51 |
| 25 |
oil quenched, fine grained, tempered at 650°C |
Tensile Strength (MPa) |
965 |
| Yield Strength (MPa) |
855 |
| Elongation (%) |
19 |
| Reduction in Area (%) |
60 |