| Conditions | Tensile Properties |
| T (°C) | Treatment |
| 25 |
annealed at 815°C |
Tensile Strength (MPa) |
722.6 |
| Yield Strength (MPa) |
275.8 |
| Elongation (%) |
17.2 |
| Reduction in Area (%) |
30.6 |
| 25 |
normalized at 855°C |
Tensile Strength (MPa) |
957.0 |
| Yield Strength (MPa) |
530.9 |
| Elongation (%) |
17.5 |
| Reduction in Area (%) |
44.8 |
| 25 |
oil quenched, fine grained, tempered at 205°C |
Tensile Strength (MPa) |
2220 |
| Yield Strength (MPa) |
1793 |
| Elongation (%) |
4 |
| Reduction in Area (%) |
10 |
| 25 |
oil quenched, fine grained, tempered at 315°C |
Tensile Strength (MPa) |
1999 |
| Yield Strength (MPa) |
1772 |
| Elongation (%) |
9 |
| Reduction in Area (%) |
30 |
| 25 |
oil quenched, fine grained, tempered at 425°C |
Tensile Strength (MPa) |
1606 |
| Yield Strength (MPa) |
1462 |
| Elongation (%) |
10 |
| Reduction in Area (%) |
37 |
| 25 |
oil quenched, fine grained, tempered at 540°C |
Tensile Strength (MPa) |
1165 |
| Yield Strength (MPa) |
1041 |
| Elongation (%) |
12 |
| Reduction in Area (%) |
47 |
| 25 |
oil quenched, fine grained, tempered at 650°C |
Tensile Strength (MPa) |
896 |
| Yield Strength (MPa) |
800 |
| Elongation (%) |
20 |
| Reduction in Area (%) |
56 |