| Conditions | Tensile Properties |
| T (°C) | Treatment |
| 25 |
annealed at 845°C |
Tensile Strength (MPa) |
564.0 |
| Yield Strength (MPa) |
372.3 |
| Elongation (%) |
29.0 |
| Reduction in Area (%) |
58.9 |
| 25 |
normalized at 870°C |
Tensile Strength (MPa) |
650.2 |
| Yield Strength (MPa) |
429.5 |
| Elongation (%) |
23.5 |
| Reduction in Area (%) |
53.5 |
| 25 |
oil quenched, fine grained, tempered at 205°C |
Tensile Strength (MPa) |
1641 |
| Yield Strength (MPa) |
1503 |
| Elongation (%) |
9 |
| Reduction in Area (%) |
38 |
| 25 |
oil quenched, fine grained, tempered at 315°C |
Tensile Strength (MPa) |
1482 |
| Yield Strength (MPa) |
1392 |
| Elongation (%) |
10 |
| Reduction in Area (%) |
42 |
| 25 |
oil quenched, fine grained, tempered at 425°C |
Tensile Strength (MPa) |
1276 |
| Yield Strength (MPa) |
1172 |
| Elongation (%) |
13 |
| Reduction in Area (%) |
47 |
| 25 |
oil quenched, fine grained, tempered at 540°C |
Tensile Strength (MPa) |
1034 |
| Yield Strength (MPa) |
896 |
| Elongation (%) |
17 |
| Reduction in Area (%) |
54 |
| 25 |
oil quenched, fine grained, tempered at 650°C |
Tensile Strength (MPa) |
772 |
| Yield Strength (MPa) |
689 |
| Elongation (%) |
23 |
| Reduction in Area (%) |
63 |