| Conditions | Tensile Properties |
| T (°C) | Treatment |
| 25 |
cold drawn (round bar (25 mm)) |
Tensile Strength (MPa) |
945 |
| Yield Strength (MPa) |
931 |
| Elongation (%) |
9 |
| Reduction in Area (%) |
43 |
| 25 |
oil quenched from 845°C, tempered at 540°C (round specimen (50 mm)) |
Tensile Strength (MPa) |
1035 |
| Yield Strength (MPa) |
910 |
| Elongation (%) |
20 |
| Reduction in Area (%) |
45 |
| 25 |
oil quenched from 845°C, tempered at 540°C (round specimen (25 mm)) |
Tensile Strength (MPa) |
1165 |
| Yield Strength (MPa) |
1000 |
| Elongation (%) |
17 |
| Reduction in Area (%) |
44 |
| 25 |
oil quenched from 845°C, tempered at 540°C (round specimen (100 mm)) |
Tensile Strength (MPa) |
889 |
| Yield Strength (MPa) |
752 |
| Elongation (%) |
23 |
| Reduction in Area (%) |
45 |
| 25 |
oil quenched from 845°C, tempered at 540°C (round specimen (75 mm)) |
Tensile Strength (MPa) |
945 |
| Yield Strength (MPa) |
814 |
| Elongation (%) |
22 |
| Reduction in Area (%) |
45 |
| 25 |
oil quenched from 845°C, tempered at 650°C (round specimen (25 mm)) |
Tensile Strength (MPa) |
972 |
| Yield Strength (MPa) |
827 |
| Elongation (%) |
16 |
| Reduction in Area (%) |
52 |
| 25 |
oil quenched from 845°C, tempered at 650°C (round specimen (100 mm)) |
Tensile Strength (MPa) |
772 |
| Yield Strength (MPa) |
635 |
| Elongation (%) |
22 |
| Reduction in Area (%) |
53 |
| 25 |
oil quenched from 845°C, tempered at 650°C (round specimen (50 mm)) |
Tensile Strength (MPa) |
848 |
| Yield Strength (MPa) |
717 |
| Elongation (%) |
19 |
| Reduction in Area (%) |
52 |
| 25 |
oil quenched from 845°C, tempered at 650°C (round specimen (75 mm)) |
Tensile Strength (MPa) |
793 |
| Yield Strength (MPa) |
655 |
| Elongation (%) |
21 |
| Reduction in Area (%) |
52 |