| Conditions | Tensile Properties |
| T (°C) | Treatment |
| 25 |
annealed at 815°C |
Tensile Strength (MPa) |
695.0 |
| Yield Strength (MPa) |
415.8 |
| Elongation (%) |
22.2 |
| Reduction in Area (%) |
46.4 |
| 25 |
normalized at 870°C |
Tensile Strength (MPa) |
929.4 |
| Yield Strength (MPa) |
606.7 |
| Elongation (%) |
16.0 |
| Reduction in Area (%) |
47.9 |
| 25 |
oil quenched, fine grained, tempered at 205°C |
Tensile Strength (MPa) |
1999 |
| Yield Strength (MPa) |
1655 |
| Elongation (%) |
10 |
| Reduction in Area (%) |
41 |
| 25 |
oil quenched, fine grained, tempered at 315°C |
Tensile Strength (MPa) |
1717 |
| Yield Strength (MPa) |
1551 |
| Elongation (%) |
11 |
| Reduction in Area (%) |
46 |
| 25 |
oil quenched, fine grained, tempered at 425°C |
Tensile Strength (MPa) |
1434 |
| Yield Strength (MPa) |
1358 |
| Elongation (%) |
13 |
| Reduction in Area (%) |
50 |
| 25 |
oil quenched, fine grained, tempered at 540°C |
Tensile Strength (MPa) |
1207 |
| Yield Strength (MPa) |
1138 |
| Elongation (%) |
15 |
| Reduction in Area (%) |
55 |
| 25 |
oil quenched, fine grained, tempered at 650°C |
Tensile Strength (MPa) |
986 |
| Yield Strength (MPa) |
903 |
| Elongation (%) |
20 |
| Reduction in Area (%) |
60 |