| AA 2024 | |
 | |
| Conditions | Tensile Properties | ||
| T (°C) | Treatment | ||
| 25 | O | Tensile Strength (MPa) | 185 |
| Yield Strength (MPa) | 76 | ||
| Elongation (%) | 20 | ||
| Reduction in Area (%) | |||
| 25 | O (Alclad) | Tensile Strength (MPa) | 180 |
| Yield Strength (MPa) | 76 | ||
| Elongation (%) | 20 | ||
| Reduction in Area (%) | |||
| 25 | T (Alclad) | Tensile Strength (MPa) | 450 |
| Yield Strength (MPa) | 310 | ||
| Elongation (%) | 18 | ||
| Reduction in Area (%) | |||
| 25 | T3 | Tensile Strength (MPa) | 485 |
| Yield Strength (MPa) | 345 | ||
| Elongation (%) | 18 | ||
| Reduction in Area (%) | |||
| 25 | T351 (Alclad) | Tensile Strength (MPa) | 440 |
| Yield Strength (MPa) | 290 | ||
| Elongation (%) | 19 | ||
| Reduction in Area (%) | |||
| 25 | T351 | Tensile Strength (MPa) | 470 |
| Yield Strength (MPa) | 325 | ||
| Elongation (%) | 20 | ||
| Reduction in Area (%) | |||
| 25 | T361 (Alclad) | Tensile Strength (MPa) | 460 |
| Yield Strength (MPa) | 365 | ||
| Elongation (%) | 11 | ||
| Reduction in Area (%) | |||
| 25 | T361 | Tensile Strength (MPa) | 495 |
| Yield Strength (MPa) | 395 | ||
| Elongation (%) | 13 | ||
| Reduction in Area (%) | |||
| 25 | T4 (Alclad) | Tensile Strength (MPa) | 440 |
| Yield Strength (MPa) | 290 | ||
| Elongation (%) | 19 | ||
| Reduction in Area (%) | |||
| 25 | T4 | Tensile Strength (MPa) | 470 |
| Yield Strength (MPa) | 325 | ||
| Elongation (%) | 20 | ||
| Reduction in Area (%) | |||
| 25 | T81 (Alclad) | Tensile Strength (MPa) | 450 |
| Yield Strength (MPa) | 415 | ||
| Elongation (%) | 6 | ||
| Reduction in Area (%) | |||
| 25 | T851 (Alclad) | Tensile Strength (MPa) | 450 |
| Yield Strength (MPa) | 415 | ||
| Elongation (%) | 6 | ||
| Reduction in Area (%) | |||
| 25 | T861 (Alclad) | Tensile Strength (MPa) | 485 |
| Yield Strength (MPa) | 455 | ||
| Elongation (%) | 6 | ||
| Reduction in Area (%) | |||