356.0 | |
![]() | |


Conditions | Tensile Properties | ||
T (°C) | Treatment | ||
25 | T51 (sand casting) | Tensile Strength (MPa) | 175 |
Yield Strength (MPa) | 140 | ||
Elongation (%) | 2.0 | ||
Reduction in Area (%) | |||
25 | T6 (permanent mold casting) | Tensile Strength (MPa) | 265 |
Yield Strength (MPa) | 185 | ||
Elongation (%) | 5.0 | ||
Reduction in Area (%) | |||
25 | T6 (sand casting) | Tensile Strength (MPa) | 230 |
Yield Strength (MPa) | 165 | ||
Elongation (%) | 3.5 | ||
Reduction in Area (%) | |||
25 | T7 (sand casting) | Tensile Strength (MPa) | 235 |
Yield Strength (MPa) | 210 | ||
Elongation (%) | 2.0 | ||
Reduction in Area (%) | |||
25 | T7 (permanent mold casting) | Tensile Strength (MPa) | 220 |
Yield Strength (MPa) | 165 | ||
Elongation (%) | 6.0 | ||
Reduction in Area (%) | |||
25 | T71 (sand casting) | Tensile Strength (MPa) | 195 |
Yield Strength (MPa) | 145 | ||
Elongation (%) | 3.5 | ||
Reduction in Area (%) |