| AA 6061 | |
 | |
| Conditions | Tensile Properties | ||
| T (°C) | Treatment | ||
| 25 | O (Alclad) | Tensile Strength (MPa) | 115 |
| Yield Strength (MPa) | 48 | ||
| Elongation (%) | 25 | ||
| Reduction in Area (%) | |||
| 25 | O | Tensile Strength (MPa) | 125 |
| Yield Strength (MPa) | 55 | ||
| Elongation (%) | 25 | ||
| Reduction in Area (%) | |||
| 25 | T4 (Alclad) | Tensile Strength (MPa) | 230 |
| Yield Strength (MPa) | 130 | ||
| Elongation (%) | 22 | ||
| Reduction in Area (%) | |||
| 25 | T4 | Tensile Strength (MPa) | 240 |
| Yield Strength (MPa) | 145 | ||
| Elongation (%) | 22 | ||
| Reduction in Area (%) | |||
| 25 | T451 (Alclad) | Tensile Strength (MPa) | 230 |
| Yield Strength (MPa) | 130 | ||
| Elongation (%) | 22 | ||
| Reduction in Area (%) | |||
| 25 | T451 | Tensile Strength (MPa) | 240 |
| Yield Strength (MPa) | 145 | ||
| Elongation (%) | 22 | ||
| Reduction in Area (%) | |||
| 25 | T6 (Alclad) | Tensile Strength (MPa) | 290 |
| Yield Strength (MPa) | 255 | ||
| Elongation (%) | 12 | ||
| Reduction in Area (%) | |||
| 25 | T6 | Tensile Strength (MPa) | 310 |
| Yield Strength (MPa) | 275 | ||
| Elongation (%) | 12 | ||
| Reduction in Area (%) | |||
| 25 | T651 (Alclad) | Tensile Strength (MPa) | 290 |
| Yield Strength (MPa) | 255 | ||
| Elongation (%) | 12 | ||
| Reduction in Area (%) | |||
| 25 | T651 | Tensile Strength (MPa) | 310 |
| Yield Strength (MPa) | 275 | ||
| Elongation (%) | 12 | ||
| Reduction in Area (%) | |||