| Conditions | Tensile Properties |
| T (°C) | Treatment |
| 25 |
annealed at 845°C |
Tensile Strength (MPa) |
463.7 |
| Yield Strength (MPa) |
341.3 |
| Elongation (%) |
31.2 |
| Reduction in Area (%) |
57.9 |
| 25 |
normalized at 925°C |
Tensile Strength (MPa) |
520.6 |
| Yield Strength (MPa) |
344.7 |
| Elongation (%) |
32.0 |
| Reduction in Area (%) |
60.8 |
| 25 |
rolled |
Tensile Strength (MPa) |
551.6 |
| Yield Strength (MPa) |
344.7 |
| Elongation (%) |
32.0 |
| Reduction in Area (%) |
57.0 |
| 25 |
water quenched, fine grained, tempered at 205°C |
Tensile Strength (MPa) |
848 |
| Yield Strength (MPa) |
648 |
| Elongation (%) |
17 |
| Reduction in Area (%) |
47 |
| 25 |
water quenched, fine grained, tempered at 315°C |
Tensile Strength (MPa) |
800 |
| Yield Strength (MPa) |
621 |
| Elongation (%) |
19 |
| Reduction in Area (%) |
53 |
| 25 |
water quenched, fine grained, tempered at 425°C |
Tensile Strength (MPa) |
731 |
| Yield Strength (MPa) |
579 |
| Elongation (%) |
23 |
| Reduction in Area (%) |
60 |
| 25 |
water quenched, fine grained, tempered at 540°C |
Tensile Strength (MPa) |
669 |
| Yield Strength (MPa) |
517 |
| Elongation (%) |
28 |
| Reduction in Area (%) |
65 |
| 25 |
water quenched, fine grained, tempered at 650°C |
Tensile Strength (MPa) |
586 |
| Yield Strength (MPa) |
441 |
| Elongation (%) |
32 |
| Reduction in Area (%) |
70 |