General Information
Further Details
Resources
Bibliography
Negotiate Your Salary

Learn the best principles to negotiate the salary you deserve!

3D Scanners

A white paper to assist in the evaluation of 3D scanning hardware solutions.

Essentials of Manufacturing

Information, coverage of important developments and expert commentary in manufacturing.

Metal 3D Printing Design Guide

Direct Metal Laser Sintering (DMLS) 3D printing for parts with reduced cost and little waste.

more free publications
 
AISI 1035
Conditions Tensile Properties 
T (°C)Treatment
25 cold drawn (round bar (50-75 mm))  Tensile Strength (MPa) 485 
Yield Strength (MPa) 415 
Elongation (%) 10 
Reduction in Area (%) 30 
25 cold drawn (round bar (22-32 mm))  Tensile Strength (MPa) 550 
Yield Strength (MPa) 485 
Elongation (%) 12 
Reduction in Area (%) 35 
25 cold drawn (round bar (19-32 mm))  Tensile Strength (MPa) 550 
Yield Strength (MPa) 460 
Elongation (%) 12 
Reduction in Area (%) 35 
25 cold drawn (round bar (32-50 mm))  Tensile Strength (MPa) 515 
Yield Strength (MPa) 450 
Elongation (%) 12 
Reduction in Area (%) 35 
25 cold drawn (round bar (16-22 mm))  Tensile Strength (MPa) 585 
Yield Strength (MPa) 515 
Elongation (%) 13 
Reduction in Area (%) 35 
25 cold drawn, high temperature, stress relieved (round bar (50-75 mm))  Tensile Strength (MPa) 450 
Yield Strength (MPa) 380 
Elongation (%) 12 
Reduction in Area (%) 35 
25 cold drawn, high temperature, stress relieved (round bar (16-22 mm))  Tensile Strength (MPa) 550 
Yield Strength (MPa) 415 
Elongation (%) 16 
Reduction in Area (%) 45 
25 cold drawn, high temperature, stress relieved (round bar (22-32 mm))  Tensile Strength (MPa) 515 
Yield Strength (MPa) 415 
Elongation (%) 15 
Reduction in Area (%) 45 
25 cold drawn, high temperature, stress relieved (round bar (32-50 mm))  Tensile Strength (MPa) 485 
Yield Strength (MPa) 415 
Elongation (%) 15 
Reduction in Area (%) 40 
25 cold drawn, low temperature, stress relieved (round bar (50-75 mm))  Tensile Strength (MPa) 515 
Yield Strength (MPa) 450 
Elongation (%) 10 
Reduction in Area (%) 30 
25 cold drawn, low temperature, stress relieved (round bar (32-50 mm))  Tensile Strength (MPa) 550 
Yield Strength (MPa) 485 
Elongation (%) 12 
Reduction in Area (%) 35 
25 cold drawn, low temperature, stress relieved (round bar (22-32 mm))  Tensile Strength (MPa) 585 
Yield Strength (MPa) 515 
Elongation (%) 12 
Reduction in Area (%) 35 
25 cold drawn, low temperature, stress relieved (round bar (16-22 mm))  Tensile Strength (MPa) 620 
Yield Strength (MPa) 550 
Elongation (%) 13 
Reduction in Area (%) 35 
25 hot rolled (round bar (19-32 mm))  Tensile Strength (MPa) 495 
Yield Strength (MPa) 275 
Elongation (%) 18 
Reduction in Area (%) 40 
25 rolled (plate (19-32 mm))  Tensile Strength (MPa) 585 
Yield Strength (MPa) 370 
Elongation (%) 30 
Reduction in Area (%) 53 
25 water quenched from 845°C, tempered at 540°C (round bar (19-32 mm))  Tensile Strength (MPa) 710 
Yield Strength (MPa) 615 
Elongation (%) 16 
Reduction in Area (%) 40 
Glossary
Negotiate Your Salary

Learn the best principles to negotiate the salary you deserve!

3D Scanners

A white paper to assist in the evaluation of 3D scanning hardware solutions.

Essentials of Manufacturing

Information, coverage of important developments and expert commentary in manufacturing.

Metal 3D Printing Design Guide

Direct Metal Laser Sintering (DMLS) 3D printing for parts with reduced cost and little waste.