| Conditions | Tensile Properties |
| T (°C) | Treatment |
| 25 |
cold drawn (round bar (16-22 mm)) |
Tensile Strength (MPa) |
655 |
| Yield Strength (MPa) |
585 |
| Elongation (%) |
12 |
| Reduction in Area (%) |
35 |
| 25 |
cold drawn (round bar (32-50 mm)) |
Tensile Strength (MPa) |
585 |
| Yield Strength (MPa) |
515 |
| Elongation (%) |
10 |
| Reduction in Area (%) |
30 |
| 25 |
cold drawn (round bar (50-75 mm)) |
Tensile Strength (MPa) |
515 |
| Yield Strength (MPa) |
485 |
| Elongation (%) |
10 |
| Reduction in Area (%) |
30 |
| 25 |
cold drawn (round bar (22-32 mm)) |
Tensile Strength (MPa) |
620 |
| Yield Strength (MPa) |
550 |
| Elongation (%) |
11 |
| Reduction in Area (%) |
30 |
| 25 |
cold drawn (round bar (19-32 mm)) |
Tensile Strength (MPa) |
625 |
| Yield Strength (MPa) |
530 |
| Elongation (%) |
12 |
| Reduction in Area (%) |
35 |
| 25 |
cold drawn, annealed (round bar (19-32 mm)) |
Tensile Strength (MPa) |
585 |
| Yield Strength (MPa) |
505 |
| Elongation (%) |
12 |
| Reduction in Area (%) |
45 |
| 25 |
cold drawn, high temperature, stress relieved (round bar (16-22 mm)) |
Tensile Strength (MPa) |
655 |
| Yield Strength (MPa) |
515 |
| Elongation (%) |
15 |
| Reduction in Area (%) |
45 |
| 25 |
cold drawn, high temperature, stress relieved (round bar (50-75 mm)) |
Tensile Strength (MPa) |
550 |
| Yield Strength (MPa) |
450 |
| Elongation (%) |
12 |
| Reduction in Area (%) |
35 |
| 25 |
cold drawn, high temperature, stress relieved (round bar (32-50 mm)) |
Tensile Strength (MPa) |
585 |
| Yield Strength (MPa) |
485 |
| Elongation (%) |
15 |
| Reduction in Area (%) |
40 |
| 25 |
cold drawn, high temperature, stress relieved (round bar (22-32 mm)) |
Tensile Strength (MPa) |
620 |
| Yield Strength (MPa) |
515 |
| Elongation (%) |
15 |
| Reduction in Area (%) |
40 |
| 25 |
cold drawn, low temperature, stress relieved (round bar (22-32 mm)) |
Tensile Strength (MPa) |
655 |
| Yield Strength (MPa) |
585 |
| Elongation (%) |
11 |
| Reduction in Area (%) |
30 |
| 25 |
cold drawn, low temperature, stress relieved (round bar (16-22 mm)) |
Tensile Strength (MPa) |
690 |
| Yield Strength (MPa) |
620 |
| Elongation (%) |
12 |
| Reduction in Area (%) |
35 |
| 25 |
cold drawn, low temperature, stress relieved (round bar (50-75 mm)) |
Tensile Strength (MPa) |
585 |
| Yield Strength (MPa) |
515 |
| Elongation (%) |
10 |
| Reduction in Area (%) |
25 |
| 25 |
cold drawn, low temperature, stress relieved (round bar (32-50 mm)) |
Tensile Strength (MPa) |
620 |
| Yield Strength (MPa) |
550 |
| Elongation (%) |
10 |
| Reduction in Area (%) |
30 |
| 25 |
hot rolled (round bar (19-32 mm)) |
Tensile Strength (MPa) |
565 |
| Yield Strength (MPa) |
310 |
| Elongation (%) |
16 |
| Reduction in Area (%) |
40 |
| 25 |
turned, ground and polished (round bar (19-32 mm)) |
Tensile Strength (MPa) |
675 |
| Yield Strength (MPa) |
405 |
| Elongation (%) |
24 |
| Reduction in Area (%) |
45 |