| Conditions | Tensile Properties |
| T (°C) | Treatment |
| 25 |
annealed at 790°C |
Tensile Strength (MPa) |
584.7 |
| Yield Strength (MPa) |
346.8 |
| Elongation (%) |
24.8 |
| Reduction in Area (%) |
41.3 |
| 25 |
normalized at 900°C |
Tensile Strength (MPa) |
667.4 |
| Yield Strength (MPa) |
399.9 |
| Elongation (%) |
21.0 |
| Reduction in Area (%) |
40.4 |
| 25 |
oil quenched, coarse grained, tempered at 650°C |
Tensile Strength (MPa) |
848 |
| Yield Strength (MPa) |
607 |
| Elongation (%) |
18 |
| Reduction in Area (%) |
42 |
| 25 |
oil quenched, coarse grained, tempered at 650°C |
Tensile Strength (MPa) |
869 |
| Yield Strength (MPa) |
621 |
| Elongation (%) |
17 |
| Reduction in Area (%) |
40 |
| 25 |
oil quenched, coarse grained, tempered at 650°C |
Tensile Strength (MPa) |
876 |
| Yield Strength (MPa) |
627 |
| Elongation (%) |
17 |
| Reduction in Area (%) |
36 |
| 25 |
oil quenched, coarse grained, tempered at 650°C |
Tensile Strength (MPa) |
724 |
| Yield Strength (MPa) |
503 |
| Elongation (%) |
23 |
| Reduction in Area (%) |
55 |
| 25 |
oil quenched, coarse grained, tempered at 650°C |
Tensile Strength (MPa) |
807 |
| Yield Strength (MPa) |
572 |
| Elongation (%) |
20 |
| Reduction in Area (%) |
46 |
| 25 |
rolled |
Tensile Strength (MPa) |
703.3 |
| Yield Strength (MPa) |
420.6 |
| Elongation (%) |
21.0 |
| Reduction in Area (%) |
41.0 |