| Conditions | Tensile Properties |
| T (°C) | Treatment |
| 25 |
annealed (wire) |
Tensile Strength (MPa) |
515 |
| Yield Strength (MPa) |
205 |
| Elongation (%) |
|
| Reduction in Area (%) |
|
| 25 |
annealed (plate, sheet, strip) |
Tensile Strength (MPa) |
515 |
| Yield Strength (MPa) |
205 |
| Elongation (%) |
40 |
| Reduction in Area (%) |
|
| 25 |
cold finished (wire) |
Tensile Strength (MPa) |
620 |
| Yield Strength (MPa) |
310 |
| Elongation (%) |
|
| Reduction in Area (%) |
|
| 25 |
cold finished and annealed (bar (over 13 mm in diameter)) |
Tensile Strength (MPa) |
515 |
| Yield Strength (MPa) |
|
| Elongation (%) |
|
| Reduction in Area (%) |
40 |
| 25 |
cold finished and annealed (bar (up to 13 mm in diameter)) |
Tensile Strength (MPa) |
620 |
| Yield Strength (MPa) |
310 |
| Elongation (%) |
30 |
| Reduction in Area (%) |
40 |
| 25 |
high tensile (bar, wire) |
Tensile Strength (MPa) |
2240 |
| Yield Strength (MPa) |
|
| Elongation (%) |
|
| Reduction in Area (%) |
|
| 25 |
high tensile, grade B (plate, sheet, strip) |
Tensile Strength (MPa) |
585 |
| Yield Strength (MPa) |
310 |
| Elongation (%) |
40 |
| Reduction in Area (%) |
|
| 25 |
high tensile, grade C (plate, sheet, strip) |
Tensile Strength (MPa) |
860 |
| Yield Strength (MPa) |
515 |
| Elongation (%) |
|
| Reduction in Area (%) |
|
| 25 |
high tensile, grade D (plate, sheet, strip) |
Tensile Strength (MPa) |
1030 |
| Yield Strength (MPa) |
760 |
| Elongation (%) |
|
| Reduction in Area (%) |
|
| 25 |
hot finished and annealed (bar) |
Tensile Strength (MPa) |
515 |
| Yield Strength (MPa) |
205 |
| Elongation (%) |
40 |
| Reduction in Area (%) |
50 |