| Conditions | Tensile Properties |
| T (°C) | Treatment |
| 25 |
annealed (wire) |
Tensile Strength (MPa) |
485 |
| Yield Strength (MPa) |
275 |
| Elongation (%) |
20 |
| Reduction in Area (%) |
45 |
| 25 |
annealed (plate, sheet, strip) |
Tensile Strength (MPa) |
450 |
| Yield Strength (MPa) |
205 |
| Elongation (%) |
22 |
| Reduction in Area (%) |
|
| 25 |
annealed, cold finished (wire) |
Tensile Strength (MPa) |
485 |
| Yield Strength (MPa) |
275 |
| Elongation (%) |
16 |
| Reduction in Area (%) |
45 |
| 25 |
annealed, cold finished (bar) |
Tensile Strength (MPa) |
485 |
| Yield Strength (MPa) |
275 |
| Elongation (%) |
16 |
| Reduction in Area (%) |
45 |
| 25 |
annealed, hot finished (bar) |
Tensile Strength (MPa) |
485 |
| Yield Strength (MPa) |
275 |
| Elongation (%) |
20 |
| Reduction in Area (%) |
45 |
| 25 |
hard temper, cold finished (bar) |
Tensile Strength (MPa) |
825 |
| Yield Strength (MPa) |
620 |
| Elongation (%) |
12 |
| Reduction in Area (%) |
40 |
| 25 |
hard temper, cold finished (wire) |
Tensile Strength (MPa) |
825 |
| Yield Strength (MPa) |
620 |
| Elongation (%) |
12 |
| Reduction in Area (%) |
40 |
| 25 |
hard temper, hot finished (bar) |
Tensile Strength (MPa) |
825 |
| Yield Strength (MPa) |
620 |
| Elongation (%) |
12 |
| Reduction in Area (%) |
40 |
| 25 |
intermediate temper, cold finished (wire) |
Tensile Strength (MPa) |
690 |
| Yield Strength (MPa) |
550 |
| Elongation (%) |
12 |
| Reduction in Area (%) |
40 |
| 25 |
intermediate temper, cold finished (bar) |
Tensile Strength (MPa) |
690 |
| Yield Strength (MPa) |
550 |
| Elongation (%) |
12 |
| Reduction in Area (%) |
40 |
| 25 |
intermediate temper, hot finished (bar) |
Tensile Strength (MPa) |
690 |
| Yield Strength (MPa) |
550 |
| Elongation (%) |
15 |
| Reduction in Area (%) |
45 |