| AISI L2 | |
 | |
| Conditions | Tensile Properties | ||
| T (°C) | Treatment | ||
| 25 | annealed | Tensile Strength (MPa) | 710 |
| Yield Strength (MPa) | 510 | ||
| Elongation (%) | 25 | ||
| Reduction in Area (%) | 50 | ||
| 25 | oil quenched from 855°C, single tempered at 205°C | Tensile Strength (MPa) | 2000 |
| Yield Strength (MPa) | 1790 | ||
| Elongation (%) | 5 | ||
| Reduction in Area (%) | 15 | ||
| 25 | oil quenched from 855°C, single tempered at 315°C | Tensile Strength (MPa) | 1790 |
| Yield Strength (MPa) | 1655 | ||
| Elongation (%) | 10 | ||
| Reduction in Area (%) | 30 | ||
| 25 | oil quenched from 855°C, single tempered at 425°C | Tensile Strength (MPa) | 1550 |
| Yield Strength (MPa) | 1380 | ||
| Elongation (%) | 12 | ||
| Reduction in Area (%) | 35 | ||
| 25 | oil quenched from 855°C, single tempered at 540°C | Tensile Strength (MPa) | 1275 |
| Yield Strength (MPa) | 1170 | ||
| Elongation (%) | 15 | ||
| Reduction in Area (%) | 45 | ||
| 25 | oil quenched from 855°C, single tempered at 650°C | Tensile Strength (MPa) | 930 |
| Yield Strength (MPa) | 760 | ||
| Elongation (%) | 25 | ||
| Reduction in Area (%) | 55 | ||