| Conditions | Tensile Properties |
| T (°C) | Treatment |
| 25 |
annealed |
Tensile Strength (MPa) |
710 |
| Yield Strength (MPa) |
510 |
| Elongation (%) |
25 |
| Reduction in Area (%) |
50 |
| 25 |
oil quenched from 855°C, single tempered at 205°C |
Tensile Strength (MPa) |
2000 |
| Yield Strength (MPa) |
1790 |
| Elongation (%) |
5 |
| Reduction in Area (%) |
15 |
| 25 |
oil quenched from 855°C, single tempered at 315°C |
Tensile Strength (MPa) |
1790 |
| Yield Strength (MPa) |
1655 |
| Elongation (%) |
10 |
| Reduction in Area (%) |
30 |
| 25 |
oil quenched from 855°C, single tempered at 425°C |
Tensile Strength (MPa) |
1550 |
| Yield Strength (MPa) |
1380 |
| Elongation (%) |
12 |
| Reduction in Area (%) |
35 |
| 25 |
oil quenched from 855°C, single tempered at 540°C |
Tensile Strength (MPa) |
1275 |
| Yield Strength (MPa) |
1170 |
| Elongation (%) |
15 |
| Reduction in Area (%) |
45 |
| 25 |
oil quenched from 855°C, single tempered at 650°C |
Tensile Strength (MPa) |
930 |
| Yield Strength (MPa) |
760 |
| Elongation (%) |
25 |
| Reduction in Area (%) |
55 |