| AISI L6 | |
 | |
| Conditions | Tensile Properties | ||
| T (°C) | Treatment | ||
| 25 | annealed | Tensile Strength (MPa) | 655 |
| Yield Strength (MPa) | 380 | ||
| Elongation (%) | 25 | ||
| Reduction in Area (%) | 55 | ||
| 25 | oil quenched from 845°C, single tempered at 315°C | Tensile Strength (MPa) | 2000 |
| Yield Strength (MPa) | 1790 | ||
| Elongation (%) | 4 | ||
| Reduction in Area (%) | 9 | ||
| 25 | oil quenched from 845°C, single tempered at 425°C | Tensile Strength (MPa) | 1585 |
| Yield Strength (MPa) | 1380 | ||
| Elongation (%) | 8 | ||
| Reduction in Area (%) | 20 | ||
| 25 | oil quenched from 845°C, single tempered at 540°C | Tensile Strength (MPa) | 1345 |
| Yield Strength (MPa) | 1100 | ||
| Elongation (%) | 12 | ||
| Reduction in Area (%) | 30 | ||
| 25 | oil quenched from 845°C, single tempered at 650°C | Tensile Strength (MPa) | 965 |
| Yield Strength (MPa) | 830 | ||
| Elongation (%) | 20 | ||
| Reduction in Area (%) | 48 | ||